Effect of surface finishing on the oxidation behaviour of a ferritic stainless steel
2017
Abstract The corrosion behaviour and the oxidation mechanism of a ferritic stainless steel, K41X (AISI 441), were evaluated at 800 °C in water vapour hydrogen enriched atmosphere. Mirror polished samples were compared to as-rolled K41X material. Two different oxidation behaviours were observed depending on the surface finishing: a protective double (Cr,Mn) 3 O 4 /Cr 2 O 3 scale formed on the polished samples whereas external Fe 3 O 4 and (Cr,Fe) 2 O 3 oxides grew on the raw steel. Moreover, isotopic marker experiments combined with SIMS analyses revealed different growth mechanisms. The influence of surface finishing on the corrosion products and growth mechanisms was apprehended by means o…
Development of hard x-ray photoelectron SPLEED-based spectrometer applicable for probing of buried magnetic layer valence states
2016
Abstract A novel design of high-voltage compatible polarimeter for spin-resolved hard X-ray photoelectron spectroscopy (Spin-HAXPES) went into operation at beamline BL09XU of SPring-8 in Hyogo, Japan. The detector is based on the well-established principle of electron diffraction from a W(001) single-crystal at a scattering energy of 103.5 eV. It's special feature is that it can be operated at a high negative bias potential up to 10 kV, necessary to access the HAXPES range. The polarimeter is operated behind a large hemispherical analyzer (Scienta R-4000). It was optimized for high transmission of the transfer optics. A delay-line detector (20 mm dia.) is positioned at the exit plane of the…
Redox-Active Ferrocene grafted on H-Terminated Si(111): Electrochemical Characterization of the Charge Transport Mechanism and Dynamics
2019
AbstractElectroactive self-assembled monolayers (SAMs) bearing a ferrocene (Fc) redox couple were chemically assembled on H-terminated semiconducting degenerate-doped n-type Si(111) substrate. This allows to create a Si(111)|organic-spacer|Fc hybrid interface, where the ferrocene moiety is covalently immobilized on the silicon, via two alkyl molecular spacers of different length. Organic monolayer formation was probed by Laser Ablation-Inductively Coupled Plasma-Mass Spectrometry (LA-ICP-MS) and X-ray photoelectron spectroscopy (XPS) measurements, which were also used to estimate thickness and surface assembled monolayer (SAM) surface coverage. Atomic force microscopy (AFM) measurements all…
Advanced Techniques of Micro-Analysis and Confocal Microscopy: Perspectives for Studying Chemical and Structural Changes at the Interface Between Res…
1995
Migration of trace amounts of elements and structural changes characterize the interface between immiscible substances. The contact zone among filling materials, saliva, and the cavity wall has the additional function of preventing the progress of leakage and subsequent caries. Difficulties in chemically and structurally analyzing the gradients of composition in an interface of microscopic dimensions characterize the experimental situation. The use of advanced techniques of instrumental micro-analysis and techniques of micro-visualization is our approach to the problem. With confocal laser scanning microscopy (CLSM), effects of the components of the filling material on the structure of the…
Magnetic dichroism in angle-resolved hard x-ray photoemission from buried layers
2011
This work reports the measurement of magnetic dichroism in angular-resolved photoemission from in-plane magnetized buried thin films. The high bulk sensitivity of hard x-ray photoelectron spectroscopy (HAXPES) in combination with circularly polarized radiation enables the investigation of the magnetic properties of buried layers. HAXPES experiments with an excitation energy of 8 keV were performed on exchange-biased magnetic layers covered by thin oxide films. Two types of structures were investigated with the IrMn exchange-biasing layer either above or below the ferromagnetic layer: one with a CoFe layer on top and another with a Co${}_{2}$FeAl layer buried beneath the IrMn layer. A pronou…
Pd–M/C (M = Pd, Cu, Pt) Electrocatalysts for Oxygen Reduction Reaction in Alkaline Medium: Correlating the Electronic Structure with Activity
2017
The increasing global needs for clean and renewable energy have fostered the design of new and highly efficient materials for fuel cells applications. In this work, Pd-M (M = Pd, Cu, Pt) and Pt nanoparticles were prepared by a green synthesis method. The carbon-supported nanoparticles were evaluated as electrocatalysts for the oxygen reduction reaction (ORR) in alkaline medium. A comprehensive electronic and structural characterization of these materials was achieved using X-ray diffraction, high-resolution transmission electron microscopy, X-ray photoelectron spectroscopy, and X-ray absorption spectroscopy. Their electrochemical properties were investigated by cyclic voltammetry, while the…
Electronic properties of Co2MnSi thin films studied by hard x-ray photoelectron spectroscopy
2009
This work reports on the electronic properties of thin films of the Heusler compound Co2MnSi studied by means of hard x-ray photoelectron spectroscopy (HAXPES). The results of photoelectron spectroscopy from multilayered thin films excited by photons of 2?8?keV are presented. The measurements were performed on (substrate/buffer layer/Co2MnSi(z)/capping layer) multilayers with a thickness z ranging from 0 to 50?nm. It is shown that high energy spectroscopy is a valuable tool for non-destructive depth profiling. The experimentally determined values of the inelastic electron mean free path in Co2MnSi increase from about 19.5 to 67?? on increasing the kinetic energy from about 1.9 to 6.8?keV. T…
Hard x-ray photoelectron spectroscopy of buried Heusler compounds
2009
This work reports on high energy photoelectron spectroscopy from the valence band of buried Heusler thin films (Co2MnSi and Co2FeAl0.5Si0.5) excited by photons of about 6?keV energy. The measurements were performed on thin films covered by MgO and SiOx with different thicknesses from 1 to 20?nm of the insulating layer and additional AlOx or Ru protective layers. It is shown that the insulating layer does not affect the high energy spectra of the Heusler compound close to the Fermi energy. The high resolution measurements of the valence band close to the Fermi energy indicate a very large electron mean free path of the electrons through the insulating layer. The spectra of the buried thin fi…
Adenosine monophosphate-capped gold(i) nanoclusters: synthesis and lanthanide ion-induced enhancement of their luminescence
2016
Reduction of Au3+ in the presence of just adenosine 5′-monophosphate (AMP) and a zwitterionic organic chemical buffering agent, specifically 4-(2-hydroxyethyl)-1-piperazineethanesulfonic acid (HEPES), combined with light exposure, gives rise to luminescent, water-soluble Au+ nanoclusters (Au+ NCs). The photoluminescence of these NCs is considerably enhanced by adding Y3+ or the chemically similar Yb3+ lanthanide that leads to Au+/Y3+ and Au+/Yb3+ NCs, respectively. These NCs are characterised by absorption (steady-state), photoluminescence (steady-state and time-resolved), and X-ray photoelectron spectroscopy.
Oxidation-driven changes of the in-plane magnetic surface anisotropies of the Fe(110)/Al interface
2003
Abstract Thin epitaxial iron films grown on W(1 1 0) were covered by ultrathin epitaxial aluminium layers of varying thicknesses from 0.2 to 0.6 nm and subsequently naturally oxidized in situ with oxygen exposures up to 150 L. Correlations between the oxidation states of the Al covers and changes of the in-plane magnetic anisotropies at the Fe(1 1 0)/Al interface were discussed on the basis of results from X-ray photoelectron spectroscopy and longitudinal magneto-optical Kerr magnetometry measurements. The Al coverage decreases the second-order in-plane surface anisotropy of the Fe(1 1 0) surface. Whereas for the thinnest Al covers, the second-order in-plane magnetic surface anisotropy decr…